A phenomenological elevated temperature friction model for viscoelastic polymer coatings based on nanoindentation

作者：Lan Pixiang; Zhang Youfeng; Dai Wei; Polycarpou Andreas A^*

来源：Tribology International, 2018, 119: 299-307.

DOI：10.1016/j.triboint.2017.11.009

• Friction model
• Viscoelastic
• Elevated temperature nanoindentation
• Polymer coating

We propose a phenomenological elevated temperature (up to 260 degrees C) friction model for viscoelastic polymer coatings based on high temperature nanoindentation. Two advanced polymeric coatings were selected for this study, namely Aromatic Thermosetting Polyester (ATSP) and Polyetheretherketone (PEEK). High temperature up to 260 degrees C nanoindentation experiments were conducted at the same temperatures as macro-scale ball-on-disk tribological experiments at different temperatures. Hardness was directly measured from the indentation experiments and viscosity/relaxation and elastic modulus were obtained by curve fitting of the nanoindentation's unloading curve using a quadratic Maxwell model. The two coatings showed decreasing hardness, elastic modulus and viscosity/relaxation trends, with increasing temperature. The ATSP coating exhibited higher indentation recovery rate and higher hardness, and thus better wear resistance.

• 出版日期2018-3