Assessment of the performance of Y2SiO5-YSZ/YSZ double-layered thermal barrier coatings

作者：Hao, Wei; Zhang, Qihui; Xing, Chen; Guo, Fangwei; Yi, Meiyu; Zhao, Xiaofeng^*; Xiao, Ping

来源：Journal of the European Ceramic Society, 2019, 39(2-3): 461-469.

DOI：10.1016/j.jeurceramsoc.2018.09.024

• Yttrium monosilicate
• Thermal barrier coatings
• Yttria-stabilized zirconia
• Lifetime
• Volume shrinkage

Y2SiO5 is a promising material for the thermal barrier coatings due to its low thermal conductivity, high temperature stability and exceptional resistance for molten silicate attack. However, it suffers low fracture toughness and low coefficient of thermal expansion compared with yttria-stabilized zirconia (YSZ). In this study, a composite coating approach, i.e., incorporating YSZ into Y(2)SiO(5 )coating, was employed to overcome those limitations. The double-layered Y2SiO5-YSZ/YSZ coatings were fabricated using atomospheric plasma spraying and tested under thermal cycling at 1150 degrees C. The phase compositions, microstructure, mechanical properties and the failure behavior were evaluated. It was found that the amorphous phase during spraying would crystallize at high temperature accompanied by volume shrinkage, leading to cracks and spallation in the coating. With YSZ addition, the composite coatings exhibited a much longer lifetime than the single phase Y2SiO5 coating due to a lower volume shrinkage and enhanced toughness.

• 出版日期2019-3
• 单位上海交通大学