Application of NR-based latex reclaim: The link between structure and properties

作者：Dierkes W K; Rajan V V; Noordermeer J W M^*; Joseph R

来源：Rubber Chemistry and Technology, 2007, 80(1): 40-60.

DOI：10.5254/1.3548168

Natural rubber based waste latex rubber (WLR) that is reclaimed with diphenyldisulphide by a thermo-mechanical process is blended with virgin rubber in different proportion to study the change in mechanical and viscoelastic properties. Two types of WLR differing mainly in the amount of polysulfidic linkages are reclaimed and blended with a virgin rubber compound with and without adjustment of the curing system, the former in order to compensate for the extra input of sulfur and accelerators due to the addition of reclaim. The cure behavior, final crosslink density and distribution, mechanical properties and dynamic viscoelastic properties of the blends with reclaimed WLR are compared to the property profile of the virgin material. The morphology of the blends as well as sulfur distribution between the matrix and the reclaim particle is analyzed.
With increasing concentrations of WLR reclaim, tensile strength, tear strength and elongation at break decrease, whereas modulus at 100% elongation, compression set and hardness show an increase. The storage modulus of the vulcanized rubber blends decreases with increasing WLR reclaim content in the blend. Swelling measurements show that the crosslink density is reduced for the adjusted cure system but increased for a fixed cure system. These influences of reclaimed WLR on the property profile of a virgin compound will be discussed fundamentally in terms of morphology and crosslink distribution.

• 出版日期2007-4