Depth-sensitive characterization of surface magnetic properties of as-quenched FeNbB ribbons

作者：Zivotsky O^*; Postava K; Hrabovska K; Hendrych A; Pistora J; Kraus L

来源：Applied Surface Science, 2008, 255(5): 3322-3327.

DOI：10.1016/j.apsusc.2008.09.044

• Amorphous and nanocrystalline magnetic materials
• Magneto-optic Kerr effect
• Scanning electron microscopy
• Depth profile

The longitudinal magneto-optical Kerr effect (MOKE) is used to study the surface magnetic properties of as-quenched FeNbB ribbons. MOKE surface hysteresis loops measured from both ribbon sides confirm different magnetic behavior. Wheel ribbon side shows heterogeneous (crystalline/amorphous) properties, thickness of crystalline phase ( about 3 nm) was established by comparing the measured magneto-optical angles of Kerr rotation and ellipticity at different incident angles with the theoretical model. Effective crystalline phase observed at shiny ribbon side is harder ( coercive field about 40 Oe) than that on wheel side and penetrates deeper into the material volume. Its thickness 1.3 mu m estimated from the weight reduction of the ribbon during surface etching is in good agreement with cross-section image obtained using the scanning electron microscopy (SEM). The sources of magnetoelastic anisotropy were identified in the bulk as well as on the ribbon surface using the magneto-optical Kerr microscopy.

• 出版日期2008-12-30