A concise water-solvent synthesis of highly effective, durable, and eco-friendly flame-retardant coating on cotton fabrics

作者：Zhang, Fengxiu; Gao, Weiwei; Jia, Yaling; Lu, Yi; Zhang, Guangxian^*

来源：Carbohydrate Polymers, 2018, 199: 256-265.

DOI：10.1016/j.carbpol.2018.05.085

• Water-solvent
• Synthesis
• Flame retardant
• Coating
• Cotton fabric
• Durability

A new halogen-free and formaldehyde-free ammonium salt of melamine hexa(methylphosphonic acid) (AMHMPA) was facilely synthesized as flame retardant (FR) material under water-solvent and low temperature condition to counter inflammable cotton fabric fire hazard. The reactive -P=O(NH4)(2) and PO(OH)(2) groups from AMHMPA reacted with cotton reactive -OH groups to form P-O-C bonds. A layer of AMHMPA was coated onto the treated-cotton surface, and a carbon skeleton was formed after combustion. The char residue percentages of the treated-cotton fabrics and untreated fabric were 38.5 and 3.6% at 600 degrees C, respectively. The phosphorus contents for the control, treated-cotton and burned-cotton were 0, 37.499 and 24.896%, respectively. The LOIs of cotton treated with 30-90 g/L AMHMPA reached 32.0-43.0%. After 50 laundering cycles (LCs), the LOIs still maintained 26.0-33.4%. AMHMPA-treated cotton had no cytotoxicity towards the environment and humans. These results demonstrated that AMHMPA-treated cotton exhibited eco-friendly, outstanding durability and excellent flame retardancy. TG-IR and cone calorimeter results confirmed AMHMPA condensation phase flame retardant mechanism.

• 出版日期2018-11-1
• 单位西南大学; 南阳理工学院