摘要
The present manuscript researches the near infrared quantum cutting luminescence phenomena of Yb3+ ion in YVO4 crystal matrix. The luminescence spectra, excitation spectra and fluorescence lifetimes were measured. It was found that the excitation of YVO4 crystal matrix energy band by 322. 0 nm light can result in the effective secondary cooperative energy transfer of Yb3+ ion from the YVO4 crystal matrix. It results in the intense 985. 5 nm F-2(5/2) -> F-2(7/2) near infrared quantum cutting luminescence of Yb3+ ion. Meanwhile, the 430. 0 nm luminescence intensity of YVO4 crystal matrix decreases greatly. From the experimental measurements, it was found that the lifetime of 430. 0 nm fluorescence of (A) Yb(1. 5) YVO4 crystal is tau(A) =3. 785 s and that of (B) YVO4 crystal is tau(B)=22. 72 s. It was found also that the theoretical efficiency up limit of quantum cutting of (A) Yb(1. 5) : YVO4 crystal is about eta(1.5%Yb) =183. 3%.
- 出版日期2015-2
- 单位中国科学院福建物质结构研究所; 北京大学; 北京师范大学