High electromagnetic interference shielding with high electrical conductivity through selective dispersion of multiwall carbon nanotube in poly (epsilon-caprolactone)/MWCNT composites

作者：Bera Ranadip; Maiti Sandip; Khatua Bhanu Bhusan^*

来源：Journal of Applied Polymer Science, 2015, 132(26): 42161.

DOI：10.1002/app.42161

• composites
• molding
• morphology

This study presents the preparation of electrically conducting poly(epsilon-caprolactone) (PCL)/multiwall carbon nanotube (MWCNT) composites with very low percolation threshold (p(c)). The method involves solution blending of PCL and MWCNT in the presence of commercial PCL beads. The PCL beads were added into high viscous PCL/MWCNT mixture during evaporation of solvent. Here, the used commercial PCL polymer beads act as an excluded volume' in the solution blended PCL/MWCNT region. Thus, the effective concentration of the MWCNT dramatically increases in the solution blended region and a strong interconnected continuous conductive network path of CNT-CNT is assumed throughout the matrix phase with the addition of PCL bead which plays a crucial role to improve the electromagnetic interference shielding effectiveness (EMI SE) and electrical conductivity at very low MWCNT loading. Thus, high EMI SE value (approximate to 23.8 dB) was achieved at low MWCNT loading (1.8 wt %) in the presence of 70 wt % PCL bead and the high electrical conductivity of approximate to 2.49x10(-2) S cm(-1) was achieved at very low MWCNT loading (approximate to 0.15 wt %) with 70 wt % PCL bead content in the composites. The electrical conductivity gradually increased with increasing the PCL bead concentration, as well as, MWCNT loading in the composites.

• 出版日期2015-7-10