AlTiN layer effect on mechanical properties of Ti-doped diamond-like carbon composite coatings

作者：Pang Xiaolu; Yang Huisheng^*; Gao Kewei; Wang Yanbin; Volinsky Alex A

来源：Thin Solid Films, 2011, 519(16): 5353-5357.

DOI：10.1016/j.tsf.2011.02.040

• Interlayer
• DLC
• AlTiN
• Tribology
• Adhesion

Ti/Ti-doped diamond-like carbon (DLC) and Ti/AlTiN/Ti-DLC composite coatings were deposited by magnetron sputtering on W18Cr4V high speed steel substrates. The effect of the AlTiN support layer on the properties of these composite coatings was investigated through microstructure and mechanical properties characterization, including hardness, elastic modulus, coefficient of friction and wear properties measured by scanning electron microscopy, Raman spectroscopy, scratch and ball-on-disk friction tests. Ti and AlTiN interlayers have a columnar structure with 50-80 nm grains. The hardness and elastic modulus of Ti/Ti-DLC and Ti/AlTiN/Ti-DLC coatings is 25.9 +/- 0.4, 222.2 +/- 6.3 GPa and 19.3 +/- 1, 205.6 +/- 6.7 GPa, respectively. Adhesion of Ti-DLC, Ti/AlTiN/Ti-DLC and AlTiN/Ti-DLC coatings expressed as the critical lateral force is 26.5 N, 38.2 N, and 47.8 N, respectively. Substrate coefficient of friction without coatings is 0.44, and it is 0.1 for Ti/Ti-DLC and Ti/AlTiN/Ti-DLC coatings. Wear resistance of Ti/AlTiN/Ti-DLC composite coatings is much higher than Ti/Ti-DLC coatings based on the wear track width of 169.8 and 73.2 mu m, respectively, for the same experimental conditions.

• 出版日期2011-6-1
• 单位北京科技大学