A facile comparative approach towards utilization of waste cotton lint for the synthesis of nano-crystalline cellulose crystals along with acid recovery

作者：Orasugh Jonathan Tersur; Saha Nayan Ranjan; Sarkar Gunjan; Rana Dipak; Mondal Dibyendu; Ghosh Swapan Kumar; Chattopadhyay Dipankar^*

来源：International Journal of Biological Macromolecules, 2018, 109: 1246-1252.

DOI：10.1016/j.ijbiomac.2017.11.123

• Cellulose
• Cotton
• Waste
• Nano-crystalline cellulose crystals
• Hemicellulose

There is a need for reuse of waste cotton lint (WCL) from the blow room of yarn spinning mills. The drive to use this material for the synthesis of nanocellulose is difficult because of the several purification/pretreatment processes. Here, we developed a combined single bath purification process of WCL and utilized it for the synthesis of nano-crystalline cellulose crystals (NCs) which are valuable nanomaterials with novel properties along with acid recovery for reuse. The micrograph of the synthesized NCs confirmed a network of nano-sized crystalline cellulose crystals having nano ranged diameter of NCs isolated by two processes. The FTIR result established the removal of impurities and hemicelluloses from WCL. The crystallinity index of WCL (similar to 89.97%) is improved to similar to 96% and similar to 94% for sulphuric acid and nitric acid synthesized NCs (NO and NC2). The crystallite size of WCL, CTWCL, NCI, and NC2 was calculated using XRD and found to be 101.56, 103.54, 98.81, and 95.6 nm respectively. The hydrodynamic size (Z-average) (d nm), polydispersity index and zeta potential of NCs was also studied using dynamic light scattering (DLS). The thermal stability of the NC1 is better than that of NC2. These NCs can be used as reinforcing filler/barrier material.

• 出版日期2018-4