Desorption-recombination behavior of as-disproportionated NdFeCoB compacts by reactive deformation

作者：Yu, Yun-Ping; Liu, Ying^*; Li, Jun; Zheng, Qing; Wang, Ren-Quan

来源：Rare Metals, 2015, 34(2): 89-94.

DOI：10.1007/s12598-014-0429-6

• NdFeB magnets
• Hydrogenation-disproportionation-desorption-recombination
• Hot deformation
• Anisotropy

The disproportionated phases of NdH (x) , Fe2B, and alpha-Fe from Nd2Fe14B were applied to prepare NdFeB magnets by two different routes. The results show that the route of annealing in horizontal vacuum sintering furnace cannot reach the purpose of complete recombination after the hot pressing and hot deformation process due to the lack of dehydrogenation channel. The route of applying low pressure of 4-25 MPa on the as-disproportionated green compact during the desorption recombination process in situ hot deformation in a spark plasma sintering (SPS) system can obtain completely recombined NdFeB magnet with good anisotropy and magnetic properties. The maximum magnetic properties, (BH)(max) = 201 kJ center dot m(-3), B (r) = 1.142 T and H (cj) = 469 kA center dot m(-1), are obtained after being treated for 15 min at 750 A degrees C under low pressure.

• 出版日期2015-2
• 单位四川大学