摘要
The microwave dielectric properties and the microstructures of (Mg1-xZnx)Al2O4 (x = 0-0.1) ceramic system prepared by the conventional solid-state route were investigated. The forming of spinel-structured (Mg1-xZnx)Al2O4 (x = 0-0.1) solid solutions was confirmed by the XRD patterns and the measured lattice parameters, which linearly varied from a = b = c = 8.0815 angstrom for MgAl2O4 to a = b = c= 8.0828 angstrom for (Mg0.9Zn0.1)Al2O4. By increasing x, the Q x f of (Mg1-xZnx)Al2O4 can be tremendously boosted from 82,000 GHz at x = 0 to a maximum of 156,000 GHz at x = 0.05. The Zn substitution was effective in reducing the dielectric loss without detrimental effects on the epsilon(r) and tau(f) values of the ceramics.
- 出版日期2011-3-3