Step Kinetics Dependent on the Kink Generation Mechanism in Colloidal Crystal Growth

作者：Nozawa Jun^*; Uda Satoshi; Guo Suxia; Toyotama Akiko; Yamanaka Junpei; Okada Junpei; Koizumi Haruhiko

来源：Crystal Growth & Design, 2018, 18(5): 2948-2955.

DOI：10.1021/acs.cgd.8b00063

Nucleation and growth of two-dimensional (2D) islands on a terrace are the dominant growth mechanisms of colloidal crystals whose particle interaction is attractive. The step velocity, v(step), of the 2D islands at various area fractions, phi(area), and polymer concentrations, C-p, has been investigated. At low C-p (weak attractive interaction between particles), there is a nearly linear relationship between v(step) and phi(area), whereas it is parabolic for high C-p (strong attraction). Depending on the C-p, two manners of kink generation at a step are observed: 1D nucleation under strong attraction and association of mound formation under weak attraction. As a result of mound formation, abundant kinks are created at steps, resulting in a linear relationship between v(step) and phi(area), whereas the relationship is parabolic for step propagation associated with 1D nucleation. Though the kink site is the most favored site for particles to be incorporated into crystals, weak attractive interaction makes the step front site an incorporation site as well, and this latter process is the main mechanism for mound formation. This study is the first to elucidate the relationship between step kinetics and the kink generation mechanism of colloidal crystals, and these new findings significantly contribute to better control of the growth of colloidal crystals.

• 出版日期2018-5