High coercivity in rare-earth lean nanocomposite magnets by grain boundary infiltration

作者：Madugundo Rajasekhar^*; Salazar Jaramillo Daniel; Manuel Barandiaran Jose; Hadjipanayis George C

来源：Journal of Magnetism and Magnetic Materials, 2016, 400: 300-303.

DOI：10.1016/j.jmmm.2015.07.019

• Hot-deformed magnet
• Grain boundary engineering
• RE-Fe-B lean permanent magnet

A significant enhancement in coercivity was achieved by grain boundary modification through low temperature infiltration of Pr-75(Cu0.25Co0.75)(25) eutectic alloy in rare-earth lean (Pr/Nd)-Fe-B/alpha-Fe nanocomposite magnets. The infiltration procedure was carried out on ribbons and hot-deformed magnets at 600-650 degrees C for different time durations. In Nd2Fe14B/alpha-Fe ribbons, the coercivity increased from 5.3 to 23.8 kOe on infiltration for 4 h. The Pr2Fe14B/alpha-Fe hot-deformed magnet shows an increase in coercivity from 5.4 to 22 kOe on infiltration for 6 h. The increase in the coercivity comes at the expense of remnant magnetization. X-ray diffraction studies confirm the presence of both the hard Nd2Fe14B and soft alpha-Fe phases. A decrease in the soft alpha-Fe phase content was observed after infiltration.

• 出版日期2016-2-15