Novel flexible broadband microwave absorptive fabrics coated with graphite nanosheets/polyurethane nanocomposites

作者：Yu, Miao-miao; Chen, Shao-hua; Zhou, Zhe; Zhu, Mei-fang^*

来源：Progress in Natural Science:Materials International , 2012, 22(4): 288-294.

DOI：10.1016/j.pnsc.2012.06.004

• Microwave absorption
• Graphite nanosheets
• Water-borne polyurethane
• Ultrasonication
• Coated fabrics

Graphitenanosheets (GNS) were prepared by surfactant assisted ultrasonication from expanded graphite (EG) and followed by coating onto vinylon fabrics with water-borne polyurethane (WPU). The morphology of GNS and GNS/polyurethane (PU) coatings was characterized by field emission scanning electron microscope (FESEM), and the structure of GNS was studied by fourier transform infrared (FTIR) spectroscopy. Electromagnetic (EM) parameters indicated that GNS is a kind of dielectric loss material, in which little magnetic loss is found. Reflection loss (RL) results showed that both GNS content and coated thickness had great influences on the microwave absorption. For the fabriccoated with GNS/PU nanocomposites (30/100 by weight, wet thickness of 0.39 mm for dry areal density in 130 g/m2), RL values exceeding -5 dB could be obtained in the frequency range of 10.718 GHz, while -10 dB in 12.718 GHz, and a minimum value of -28 dB at 15.2 GHz. These GNS/PU coatedfabrics are light and flexible with much thin and low-cost coated layer, and showed great potential in radar camouflaging and electromagnetic interference application.

• 出版日期2012-8
• 单位东华大学