An efficient lithium ion imprinted adsorbent using multi-wall carbon nanotubes as support to recover lithium from water

作者：Huang, Yan; Wang, Rui^*

来源：Journal of Cleaner Production, 2018, 205: 201-209.

DOI：10.1016/j.jclepro.2018.09.076

• Adsorption
• Crown ether
• Lithium
• Multi-wall carbon nanotubes
• Selectivity
• Surface imprinting

With the extensive applications of lithium ion batteries, the exploitation and recycle of lithium resources is essential for the manufacture of lithium ion batteries. This work reports that novel lithium ion imprinted polymers (LIPs) loaded on the surface of multi-wall carbon nanotubes (MWCNTs were prepared by surface imprinting polymerization. The performance of the prepared LIPs was analyzed by UV-vis recording spectrophotometry, ICP-AES, MIR and SEM. The maximum adsorption capacity of the 15 mg LIPs was calculated to be 1362.56 mu mol/g at a 300 mg/L Li+ solution. In the presence of Na+, K+, Cu2+ and Zn2+, the selectivity factors of the LIPs for Li+ were 3.66, 3.01, 2.05 and 2.10, respectively, suggesting that the LIPs had ideal selectivity for Li+. In addition, the experimental data can be described well by the pseudo-first-order and Langmuir adsorption isotherm models. The regeneration of the LIPs was performed by being eluted with 1 M nitric acid, and the adsorption capacity of the regenerated LIPs only decreased about 10.3% after ten cycle experiments. Therefore, the strategy described in this work is worth further exploring its application on the extraction and separation of lithium to realize the recovery utilization of lithium in water.

• 出版日期2018-12-20
• 单位山东大学