Aligned InN nanofingers prepared by the ion-beam assisted filtered cathodic vacuum arc technique

作者：Ji XH^*; Lau SP; Yang HY; Yu SF

来源：Nanotechnology, 2005, 16(12): 3069-3073.

DOI：10.1088/0957-4484/16/12/057

We report the synthesis of aligned wurtzite InN nanofingers by the ion-beam assisted filtered cathodic vacuum arc technique. InN nanofingers exhibit a polycrystalline structure. Photoluminescence (PL) and field emission properties of the InN nanofingers were studied. The PL emission peak was centred at similar to 1. 1 eV with a full width at half maximum of 105 meV. The field emission characteristic was observed from the InN nanofingers with turn-on field of 9.7 V mu m(-1\) at a current density of 10 mu A cm(-2). The formation of InN nanofingers was attributed to the Volmer-Weber growth mode.