Submicron alumina based magnetic tunnel junctions (MTJs) using electrodes with out-of-plane magnetic anisotropy were prepared and characterized. Both electrodes are industry-compatible Co/Pt multilayers. The magnetic properties of the unpatterned samples have been investigated through superconducting quantum interference device (SQUID) magnetometry and extraordinary Hall effect: both electrodes have fully out-of-plane magnetic moments and nonoverlapping coercive fields. Transport measurements on the submicron MTJs showed a magnetoresistance (MR) ratio reaching 8% at room temperature. Nanopillars with diameters of 800, 400, and 200 nm patterned from the same wafer show the expected out-of-plane magnetic properties and similar resistancexarea products (RA) and MR ratios. The I(V) characteristics of pillars with diameters of 800 and 400 nm could be accounted for with reasonable barrier heights and widths.