Mechanical properties of Mg-Al-Ca alloy processed by hot extrusion

作者：Watanabe Hiroyuki^*; Yamaguchi Masahiro; Takigawa Yorinobu; Higashi Kenji

来源：Materials Science and Engineering A-Structural Materials Properties Microstructure and Processing, 2007, 454: 384-388.

DOI：10.1016/j.msea.2006.12.130

• magnesium alloy
• extrusion
• strength
• high temperature deformation
• dislocation creep
• constitutive equation

Mechanical properties of hot extruded Mg-6 mass%Al-2 mass%Ca alloy were examined. The alloy was homogenized at 723 K for 24 h before extrusion in order to dissolve the second phase, Al(2)Ca. The grain size of the extruded sheet was 15 mu m and spherical particles with the size of 1.5 mu m were dispersed mainly in the grain boundaries. The ductility at room temperature was high compared with other magnesium alloys containing Ca. The ductility was enhanced at above 623 K. It was suggested that climb controlled dislocation creep could be a dominant deformation process at elevated temperatures and at around 10(-1) s(-1). The constitutive equation for high temperature deformation was also developed.

• 出版日期2007-4-25