Structure-property relationships in copolyester elastomer-layered silicate nanocomposites

作者：Alosime Eid M; Edwards Grant A; Martin Darren J^*

来源：Journal of Applied Polymer Science, 2015, 132(13): 41742.

DOI：10.1002/app.41742

• creep resistance
• organoclay
• thermoplastic polyester elastomer
• water vapour permeability

While the field of polymer-clay nanocomposites is reaching maturity, some parts of the studied systems still present researchers with possibilities for the improvement of material properties. This study entails the understanding of the relationships in copolyester elastomer/organically modified layered silicate nanocomposite and the structure-property relationships within the system of the nanocomposite. A series of these nanocomposites was prepared via twin-screw extrusion melt compounding. The experiments included the following three types of synthetic organosilicates: high aspect ratio Somasif (ME100) fluoromica and two lower aspect ratio Laponite synthetic hectorites, (WXFN) and (WXFP). These organosilicates were modified with quaternary octadecyltrimethylammonium bromide (ODTMA) and were used to prepare the nanocomposites. The nanocomposite structure on a micro- and nanometre scales was evaluated by two techniques, such as X-ray diffraction (XRD) and transmission electron microscopy (TEM). The mechanical properties of the nanocomposites were examined to determine the impact aspect ratio of the nanofiller and wt % loading have on performance. The addition of the 2 wt % high aspect ratio of ME100-ODTMA, in particular, showed statistically improved tensile strength, tear resistance, creep resistance, and water vapor permeation barrier enhancement.

• 出版日期2015-4-5