To probe the microstructures of nitrate ester plasticized polyether (NEPE) composite propellants and observe the morphology of each constitute in the propellant, the microstructure and elemental constitutes of NEPE propellants were investigated using, scanning electron microscopy and energy dispersive X-ray spectroscopy. The ammonium perchlorate (AP) grains had a scraggy surface and were difficult to disperse uniformly. The compatibility between the AP grains and the polymer binder was poor, especially for large grains. The size distribution range of the AP and octogen (HMX) grains in propellants varied from several to several hundreds pm for the former while for the latter from several to several tens pm. Contrasting images before and after dissolution the propellant in trichloromethane showed that the degree of crosslinking of the polymer binder was low since non-crosslinked binder on the surface areas was easily removed by the solvent, and that the plasticizer was near the HMX grains and contributed more O to the element analysis of HMX.