All-Nonvacuum-Processed CIGS Solar Cells Using Scalable Ag NWs/AZO-Based Transparent Electrodes

作者：Wang Mingqing; Choy Kwang Leong^*

来源：ACS Applied Materials & Interfaces, 2016, 8(26): 16640-16648.

DOI：10.1021/acsami.6b02137

• CIGS solar cells
• Ag nanowires
• nonvacuum
• transparent conducting electrode
• nanocomposite

With record cell efficiency of 21.7%, CIGS solar cells have demonstrated to be a very promising photovoltaic (PV) technology. However, their market penetration has been limited due to the inherent high cost of the cells. In this work, to lower the cost of CIGS solar cells, all nonvacuum-processed CIGS solar cells were designed and developed. CIGS absorber was prepared by the annealing of electrodeposited metallic layers in a chalcogen atmosphere. Nonvacuum-deposited Ag nanowires (NWs)/AZO transparent electrodes (TEs) with good transmittance (92.0% at 550 nm) and high conductivity (sheet resistance of 20 Omega square) were used to replace the vacuum -sputtered window layer. Additional thermal treatment after device preparation was conducted at 220 degrees C for a few of minutes to improve both the value and the uniformity of the efficiency of CIGS pixel cell on 5 X 5 cm substrate. The best performance of the all-nonvacuum-fabricated CIGS solar cells showed an efficiency of 14.05% with Jsc of 34.82 mA/cm(2), Voc of 0.58 V, and FF of 69.60%, respectively, which is comparable with the efficiency of 14.45% of a reference cell using a sputtered window layer.

• 出版日期2016-7-6