Morphology Changes in Bulk Donor-Acceptor Poly(Benzodithiophene-Benzotriazole) after Post-Treatment

作者：Zajaczkowski Wojciech; Marszalek Tomasz; Wong Wallace W H; Pisula Wojciech^*

来源：Journal of Polymer Science Part B: Polymer Physics , 2016, 54(22): 2327-2334.

DOI：10.1002/polb.24143

• morphology
• self-assembly
• annealing
• conjugated polymer
• WAXS

The bulk order in donor-acceptor poly(benzodithiophene-benzotriazole) was improved by two different post-treatment procedures applied to the specimen. Two-dimensional wide-angle X-ray scattering was used to investigate the structural changes after treatment. After post-treatment the polymer turned into a highly crystalline morphology with well-resolved and intensive p-stacking reflections which were absent in the pristine sample. To understand the ordering mechanisms taking place during the two post-treatment procedures, structural parameters like coherence length and paracrystallinity were extracted from the Xray data indicating the impact on crystallite size and cumulative lattice disorder. During temperature annealing the intralayer packing transforms from amorphous to highly ordered. On the other hand, solvent vapor annealing enhances in higher extent the interlayer organization due to interpenetration of solvent molecules between alkyl side chains. These results provide important insights for the morphology optimization of semicrystalline conjugated polymers.

• 出版日期2016-11