Analysis of microstructure and strengthening in pure titanium recycled from machining chips by equal channel angular pressing using electron backscatter diffraction

作者：Luo P; McDonald D T^*; Zhu S M; Palanisamy S; Dargusch M S; Xia K

来源：Materials Science and Engineering A-Structural Materials Properties Microstructure and Processing, 2012, 538: 252-258.

DOI：10.1016/j.msea.2012.01.039

• Titanium
• Recycling
• Equal channel angular pressing (ECAP)
• Electron backscatter diffraction (EBSD)
• Machining chips
• Hall-Petch relationship

Equal channel angular pressing (ECAP) was used to realise solid-state recycling of pure titanium machining chips. Fully dense bulk Ti with ultrafine grain sizes was obtained after ECAP at 450 degrees C although the grains were coarser at the higher consolidation temperature of 590 degrees C. The yield strength of the recycled Ti obeys the Hall-Petch relationship and reaches 650 MPa after consolidation at 450 degrees C for two passes. The strengths achieved are comparable to those observed in other Ti produced by ingot metallurgy with similar grain sizes. Analyses show that the strengthening is primarily due to grain size refinement rather than oxide dispersion, and low angle grain boundaries make significant contributions especially at the lower processing temperature.

• 出版日期2012-3-15
• 单位中国空间技术研究院