A copper and chromium based nanoparticulate oxide as a noble-metal-free cocatalyst for photocatalytic water splitting

作者：Maeda Kazuhiko; Ohno Tomoyuki; Domen Kazunari^*

来源：Chemical Science, 2011, 2(7): 1362-1368.

DOI：10.1039/c1sc00177a

Nanoparticulate oxides consisting of copper (Cu) and chromium (Cr) were studied as noble-metal-free cocatalysts for photocatalytic water splitting. The structure of the Cu-Cr mixed oxide dispersed on a solid solution of GaN and ZnO (referred to as GaN : ZnO hereafter) was characterized by high-resolution transmission electron microscopy (HR-TEM), X-ray absorption fine-structure (XAFS) spectroscopy, and electrochemical measurements. The mixed-oxide nanoparticle was an effective promoter of photocatalytic overall water splitting on GaN : ZnO, and was loaded by impregnation from an aqueous solution containing Cu(NO(3))(2)center dot 3H(2)O and Cr(NO(3))(3)center dot 9H(2)O followed by calcination in air. Impregnation of GaN : ZnO with 1.5 wt% Cu and 2.0 wt% Cr followed by calcination at 623 K for 1 h provided the highest photocatalytic activity, while catalysts modified with either Cu-oxide or Cr-oxide showed little activity. The activity of this photocatalyst was shown to be strongly dependent on the generation of Cu(II)-Cr(III) mixed-oxide nanoparticles with optimal composition and coverage. The results of electrochemical measurements and photocatalytic reactions also indicated that Cu(II)-Cr (III) mixed-oxide nanoparticles on GaN : ZnO are resistant to both the photoreduction of O(2) and water formation from H(2) and O(2), which are undesirable reverse reactions in overall water splitting.

• 出版日期2011