The Essential Work of Fracture of Thermoplastic Orthodontic Retainer Materials

作者：Pascual Albert L; Beeman Cynthia S^*; Hicks E Preston; Bush Heather M; Mitchell Richard J

来源：The Angle Orthodontist, 2010, 80(3): 554-561.

DOI：10.2319/042809-232.1

• Essential
• Work
• Fracture
• Orthodontic
• Thermoplastic
• Retainer

Objective: To investigate whether oral cleansing agents affect the essential work of fracture (EWF) and plastic work of fracture (PWF) for two types of orthodontic thermoplastic retainer materials. Materials and Methods: Polyethylene-terephthalate-glycol (PETG; Tru-Tain Splint) and polypropylene/ethylene-propylene rubber (PP-EPA) blend (Essix-C+) sheets were compared. For each material, six sets of 25 sheets were thermoformed into double-edge-notched-tension specimens; subsets of five specimens were formed with internotch distances (L) equal to 6, 8, 10, 12, or 14 mm, respectively. Sets were stored (160 hours, 25 degrees C) in air (DRY), distilled water (DW), Original Listerine (LIS), mint Crest Pro Health (CPH), 3% hydrogen peroxide (HP), or Polident solution (POL). Specimens were fractured in tension at 2.54 mm/min. Areas under load-elongation curves were measured to determine total work of fracture (W(f)). Linear regressions (W(f) vs L [n = 25]) yielded intercepts (EWF) and slopes (PWF). Ninety-five percent confidence intervals were used to evaluate differences in EWF and PWF estimates. Results: PP-EPR blends showed higher EWFs after storage in HP vs storage in DW. PP-EPA blend showed higher EWFs after storage in CPH vs PETG. After HP storage, PP-EPA exhibited lower PWFs than with any other storage conditions. PP-EPR exhibited higher PWFs than PETG after storage in DRY, DW, and LIS. Conclusions: Compared with DW, none of the cleansers decreased the energy to initiate fracture. With one exception, no cleanser decreased the energy to continue plastic fracture extension. In PP-EPA blend, increased resistance to fracture initiation was observed with CPH and HP, yet, surprisingly, HP decreased resistance to plastic fracture growth. (Angle Orthod. 2010;80:554-561.)

• 出版日期2010-5