Ultrasonic semi-solid coating soldering 6061 aluminum alloys with Sn-Pb-Zn alloys

作者：Yu Xin-ye; Xing Wen-qing; Ding Min^*

来源：Ultrasonics Sonochemistry, 2016, 31: 216-221.

DOI：10.1016/j.ultsonch.2016.01.004

• Crystallization behavior
• Ultrasonic semi-solid coating soldering
• 6061 aluminum alloy
• Shear strength

In this paper, 6061 aluminum alloys were soldered without a flux by the ultrasonic semi-solid coating soldering at a low temperature. According to the analyses, it could be obtained that the following results. The effect of ultrasound on the coating which promoted processes of metallurgical reaction between the components of the solder and 6061 aluminum alloys due to the thermal effect. Al2Zn3 was obtained near the interface. When the solder was in semi-solid state, the connection was completed. Ultimately, the interlayer mainly composed of three kinds of microstructure zones: alpha-Pb solid solution phases, beta-Sn phases and Sn-Pb eutectic phases. The strength of the joints was improved significantly with the minimum shear strength approaching 101 MPa.

• 出版日期2016-7
• 单位太原理工大学