Use of a design-of-experiments approach for preparing ceria-zirconia-alumina samples by sol-gel process

作者：Dumont Marcello R^*; Nunes Eduardo H M; Vasconcelos Wander L

来源：Ceramics International, 2016, 42(8): 9488-9495.

DOI：10.1016/j.ceramint.2016.03.021

• Sol-gel processes
• Al2O3
• CeO2
• ZrO2

In this work we successfully obtained ceria-zirconia-alumina samples by the sol-gel technique. These materials were prepared under acidic or basic conditions, using either nitric acid or ammonium hydroxide as the catalyst. A design-of-experiments approach was used in order to optimize the specific surface area, pore structure, and thermal stability of the prepared samples. It was observed that the addition of ceria and zirconia did not affect the formation of gamma-Al2O3. The highest surface areas and smallest pore sizes were observed for specimens obtained under acidic conditions and with low to intermediate concentrations of cerium and water. The increase of the heat treatment temperature from 600 degrees C to 1000 degrees C led to both a decrease of the surface area and an increase of the mean pore size. This behavior is due to the coalescence of pores upon calcination. Samples with a high concentration of ceria showed an expressive thermal instability at high temperatures. On the other hand, the addition of zirconia increased the thermal stability of these materials. In general, samples with improved thermal stabilities were obtained under basic conditions.

• 出版日期2016-6