It is shown that chromium distribution in the metal base of high-chromium cast irons depends on manganese content. According to the X-ray micro-spectral analysis data with the increase of manganese content from 0.72 to 6.49% chromium content decreased in the near-carbide zones. At the same time chromium content in carbides increased. This process obtained particularly strong development inside eutectic colonies of carbides. As a result of it, when total chromium content in the alloy has been 23%, its concentration in the local zones was 12,3%, thus the necessary level of corrosion resistance has not been provided. The minimal chromium content has to amount 23.2%, at 6.49% Mn and 2.2...2.5% C in order to provide corrosion resistance of high-chromium cast irons.
- 出版日期2013