A New Creep Test Method for Asphalt Mixtures

作者：Huang, Xiaoming^*; Zhang, Yuqing

来源：Road Materials and Pavement Design, 2010, 11(4): 969-991.

DOI：10.3166/RMPD.11.969-991

• Partial Triaxial Test
• Creep Test
• Permanent Deformation
• Asphalt Mixtures

A new creep test, Partial Triaxial Test (PTT), was developed to study the permanent deformation properties of asphalt mixtures. The PTT used two duplicate platens whose diameters were smaller than the diameter of the cylindrical asphalt mixtures specimen. One base platen was centrally placed under the specimen and another loading platen was centrally placed on the top surface of the specimen. Then the compressive repeated load was applied on the loading platen and the vertical deformation of the asphalt mixture was recorded in the PTTs. Triaxial repeated load permanent deformation tests (TRT) and PTTs were respectively conducted on AC20 and SMA13 asphalt mixtures at 40 degrees C and 60 degrees C so as to provide the parameters of the creep constitutive relations in the ABAQUS finite element models (FEMs) which were built to simulate the laboratory wheel tracking tests. The real laboratory wheel tracking tests were also conducted on AC20 and SMA13 asphalt mixtures at 40 degrees C and 60 degrees C. Then the calculated rutting depth from the FEMs were compared with the measured rutting depth of the laboratory wheeling tracking tests. Results indicated that PTT was able to characterize the permanent deformation of the asphalt mixtures in laboratory. The rutting depth calculated using the parameters estimated from PTTs' results was closer to and showed better matches with the measured rutting than the rutting depth calculated using the parameters estimated from TRTs' results. Main reason was that PTT could better simulate the changing confinement conditions of asphalt mixtures in the laboratory wheeling tracking tests than the TRT.

• 出版日期2010-12
• 单位东南大学