The components of a gas turbine operate in an aggressive environment where the temperature of service varies from ambient to near melting point of materials which introduce a variety of degradation on the components. Some components that lose their dimensional tolerance during use require repair and refurbishment when high cost replacement is avoidable. Erosion of fly ash and sand particles damages compressor blades which cause engine failure at an early stage. Dovetail roots of the compressor blades are subjected to fretting fatigue due to the oscillatory motion caused by vibration. Casing of the compressor comes in contact with rotating blades due to shaft misalignment, ovality of the casing and or inadequate clearance which cause blade and casing damage. Close clearance control that has bearing on the efficiency of the engine is therefore required in addition to preventing fire where titanium to titanium rubbing might occur. Wear out of the several contact surfaces which undergo rotating and reciprocating motion occur during the running of the engine need protection. Hot gases that are produced by burning the contaminated fuel in the combustion chamber will cause oxidation and corrosion on their passage. In the hot section rotating and stationary components need thermal insulation from higher operating temperature leading to enhanced thermodynamic efficiency of the engine. This wide range of functional requirements of the engine is met by applying an array of coatings that protect the components from failures. Current overview, while not aiming at deeper insight into the field of gas turbine coatings, brings out a summary of details of these coatings at one place, methods of application and characterization, degradation mechanisms and indicative future directions which are of use to a practicing industrial engineer.
- 出版日期2012-12