摘要
Co-B doped NaAlH4 is successfully synthesized by two-step synthesis process. The first activation step is milling NaH/Al powder and Co-B mixtures under Ar atmosphere. The second step is milling in a lower hydrogen pressure atmosphere. XRD patterns and FTIR spectrum demonstrate that NaAlH4 is completely formed after 15 h milling in Ar atmosphere following by 40 h milling in 2 MPa H-2 atmosphere. PCT curves of as-prepared NaAlH4 show that it can release hydrogen at a low temperature of 90 degrees C. The activation energy value calculated by Arrhenius equation is only 67.95 kJ mol(-1). Moreover, the formation mechanism of NaAlH4 is also discussed.
- 出版日期2010-10
- 单位南开大学