Pyrolysis kinetics of olive residue/plastic mixtures by non-isothermal thermogravimetry

作者：Aboulkas A^*; El Harhi K; El Bouadili A; Nadifiyine M; Benchanaa M; Mokhlisse A

来源：Fuel Processing Technology, 2009, 90(5): 722-728.

DOI：10.1016/j.fuproc.2009.01.016

• Pyrolysis
• Kinetics
• Olive residue
• Plastic
• Olive residue/plastic mixtures

The TGA studies of a pyrolytic decomposition of mixtures of olive residue/plastic were carried out. The investigation was made at the temperature ranging from 300 to 1273 K) in the nitrogen atmosphere at four heating rates beta = 2. 10, 20 and 50 K min(-1). High density polyethylene (HDPE), low density polyethylene (LDPE), polypropylene (PP) and polystyrene (PS) were selected as plastic samples. Based on the results obtained, three thermal stages were identified during the thermal degradation. The first two were dominated by the olive residue pyrolysis, while the third was linked to the plastics pyrolysis, which occurred at much higher temperatures. Discrepancies between the experimental and calculated TG/DTG profiles were considered as a measurement of the extent of interactions occurring on pyrolysis olive residue/plastic mixtures. The maximum degradation temperatures of each component in the mixture were higher than those of the individual components. These experimental results indicate a significant synergistic effect during olive residue and plastic co-pyrolysis at the high temperature region. In addition, a kinetic analysis was performed to fit thermogravimetric data. A reasonable fit to the experimental data was obtained for all materials and their mixtures.

• 出版日期2009-5