A comparative study on the performance of suspension plasma sprayed thermal barrier coatings with different bond coat systems

作者：Zou, Zhonghua; Donoghue, Jack; Curry, Nicholas; Yang, Lixia; Guo, Fangwei; Nylen, Per; Zhao, Xiaofeng^*; Xiao, Ping

来源：Surface and Coatings Technology, 2015, 275: 276-282.

DOI：10.1016/j.surfcoat.2015.05.006

• Thermal barrier coatings
• Suspension plasma spray
• Bond coat
• Isothermal exposure
• Stress

The performance of suspension plasma sprayed (SPS) yttria stabilized zirconia (YSZ) thermal barrier coatings (TBCs) after isothermal treatment at 1150 degrees C was investigated. The NiCoCrAlY bond coats were applied by air plasma spray (APS) and high velocity oxygen fuel (HVOF) techniques. It was found that the microstructure of SPS TBCs depends on the surface morphology of the bond coat. The SPS TBCs with a rough APS bond coat exhibited a longer lifetime than those with a smooth HVOF bond coat. To understand this phenomenon, the evolution of the microstructure, mechanical properties and the residual stresses in the TBCs and TGO were systematically studied. Results showed that the surface roughness and oxidation behavior of the bond coat play dominant roles in the SPS TBC failure.

• 出版日期2015-8-15
• 单位上海交通大学