Strength and fracture of two hot-rolled Ti-Al-Si-Nb dual phase alloys based on Ti3Al

作者：Zhang, LT^*; Wu, JS; Hua, W; Qiu, GH

来源：Intermetallics, 2000, 8(7): 709-716.

DOI：10.1016/S0966-9795(99)00123-5

• multiphase intermetallics
• titanium aluminides, based on Ti3Al
• fracture mode
• mechanical properties at ambient temperatures
• mechanical properties at high temperatures
• rolling

Ti-Al-Si-Nb dual phase alloys are mainly composed of alpha(2)-Ti3Al matrix and Ti5Si3 silicide phases. In this paper, two alloys (402 and 405) whose Si contents are 2 and 5 at% respectively were are melted and hot-rolled into sheets with different amounts of deformation. The silicide phase (Ti,Nb)(5)(Si,Al)(3) was broken up into small pieces and redistributed in the alpha(2) matrix during the hot-rolling. improved strength and ductility of the two alloys were observed after hot-rolling, which can be attributed to both the finely distributed reinforcement silicide phase and refinement of the matrix grain size. The mechanical properties of the two alloys are dependent on their volume fractions of the silicide phase: the strength of alloy 405 is higher than that of alloy 402, while alloy 402 is more ductile than alloy 405. The brittle-ductile transition temperature of the two dual phase alloys is between 600 and 800 degrees C. The surface slip on the dual phase alloys was also observed. Obvious separation between the (Ti,Nb)(5)(Si,Al)(3) particles and the alpha(2) matrix is found on the fracture surfaces obtained at high temperature, showing dimple-like morphology.

• 单位
  上海交通大学