Mechanical performance of oxidized Zr-Nb-O nuclear cladding tubes

作者：Jeong Gu Beom^*; Choi Yong; Hong Sun Ig

来源：Physics of Metals and Metallography, 2014, 115(13): 1281-1284.

DOI：10.1134/S0031918X14130079

• Zr-Nb-O
• Fuel cladding
• Oxidation
• mechanical properties
• Ring compression
• ring tension

Ring compression and tensile tests on oxidized Zr-Nb-O cladding tubes were performed, to examine the reliability of nuclear cladding tubes after oxidation. The oxidation rate was observed to be far greater at 700A degrees C than 600A degrees C, because of the increased volume fraction of less protective porous oxide. The tensile strength of oxidized Zr-1Nb cladding tubes at 600A degrees C for 3 h increased, with no appreciable loss of ductility. After heat treatment at 600A degrees C for 24 h and 700A degrees C for 3 h, the yield strength and the initial flow stress increased, and the flow stress decreased rapidly with strain, resulting in decreased ductility. The increase of yield strength after heat treatment at 600A degrees C in Zr-1Nb was associated with the presence of strong and protective oxide film. In compressive loading, for cladding tubes oxidized at 600A degrees C for 24 h and 700A degrees C for 3 h, a small drop of load, resulting from cracking of the surface oxide layer, was observed at the total displacement of 1.3 similar to 1.5 mm. The catastrophic fracture that was observed at the total displacement of 5.7 mm in Zr-Nb-Sn-Fe did not occur in Zr-Nb-O. The absence of sudden drop and catastrophic fracture at the displacement of 5 similar to 7 is thought to be associated with the softer matrix of annealed Zr-Nb-O.

• 出版日期2014-12