An attempt to predict the mechanism of Mo-Ni-O powders electrodeposition from the results of their TEM analysis

作者：Jovic V D^*; Jovic B M; Lacnjevac U; Brankovic G; Bernik S; Recnik A

来源：Electrochimica Acta, 2010, 55(13): 4188-4193.

DOI：10.1016/j.electacta.2010.02.065

• Electrodeposited Mo-Ni-O powder
• TEM
• Amorphous
• Crystalline
• Phase composition

The Mo-Ni-O powders were electrodeposited from ammonium sulfate containing electrolytes with different Mo/Ni ion concentration ratios. The phase composition of these powders was investigated using TEM. EDS and XRD analysis. The TEM analysis showed that two types of particles were present in the powders: amorphous and crystalline. For crystalline particles it was found that two phases, MoO(3) and MoNi(4) prevail in all powders, while the NiO phase was detected in the powder electrodeposited at Mo/Ni = 0.3/1. These findings are in good agreement with our previous results where MoO(3), MoNi(4) and NiMoO(4) phases were detected in the recrystallized Mo-Ni-O powders. In this work we discovered that the NiMoO(4) phase was formed by solid state reaction between NiO and MoO(3) at elevated temperature.

• 出版日期2010-5-1