摘要
Static and dynamic properties of (CoO/CoFeB)(n) multilayers have been investigated. An anisotropy field enhancement was evidenced when the CoO layer was deposited under the CoFeB layer. Tuning the relative CoFeB and CoO layers thicknesses, high ferromagnetic resonance frequencies up to 4 GHz were achieved. The coupling effect between the CoO and CoFeB layers was induced by a dipolar coupling due to the anisotropic roughness topology of the CoO layer. This anisotropic roughness was induced by the deposition geometry and evidenced by atomic force microscopy. The strength of the dipolar interfacial coupling was calculated thanks to Schlomann's model. Multilayer stacks were fabricated and the magnetic properties observed for the trilayers could be maintained.
- 出版日期2015-1-21
- 单位中国地震局