An investigation into the effect of fabric structure on the compressional properties of woven fabrics

作者：Asayesh Azita^*; Mirgoli Farimah; Gholamhosseini Alireza

来源：Journal of the Textile Institute, 2018, 109(1): 32-38.

DOI：10.1080/00405000.2017.1320817

• Woven fabric
• compression
• weft density
• weave pattern
• thickness
• pressure

Lateral compression is one of the most important mechanical aspects of fabrics, which reflects their handle. Fabric compressional features depend on the compressional characteristics of constituent yarns and the fabric structure. In order to consider the effect of fabric structural parameters on its compressional properties, woven fabrics with five different weave patterns (plain, hopsack 2/2, twill 2/2, twill 3/1, warp rib 2/2) were produced with three different nominal weft densities (12, 15, 18cm(-1)). The compressional properties of produced fabrics were evaluated at different pressure values using a conventional fabric thickness tester. It was observed that increasing the weft density leads to decrease in the dissipated compression energy as well as the compressibility of the fabric, while the thickness recovery of the fabric increases. Moreover, the plain woven fabric exhibited the lowest dissipated compression energy and compressibility, while the highest thickness recovery. Besides, at the low pressure level, the fabrics with the lower weft densities demonstrate the higher thickness. By increase in the pressure level, the fabric thickness decreases by decreasing the weft density.

• 出版日期2018