A Systematic Study of the Structural and Magnetic Properties of Mn-, Co-, and Ni-Doped Colloidal Magnetite Nanoparticles

作者：Deepak Francis Leonard; Banobre Lopez Manuel; Carbo Argibay Enrique; Fatima Cerqueira M; Pineiro Redondo Yolanda; Rivas Jose; Thompson Corey M; Kamali Saeed; Rodriguez Abreu Carlos; Kovnir Kirill; Kolen'ko Yury V^*

来源：Journal of Physical Chemistry C, 2015, 119(21): 11947-11957.

DOI：10.1021/acs.jpcc.5b01575

A series of colloidal MxFe3-xO4 (M = Mn, Co, Ni; x = 0-1) nanoparticles with diameters ranging from 6.8 to 11.6 nm was synthesized by hydrothermal reaction in aqueous medium at low temperature (200 degrees C). Energy-dispersive X-ray microanalysis and inductively coupled plasma spectrometry confirm that the actual elemental compositions agree well with the nominal ones. The structural properties of the obtained nanoparticles were investigated by powder X-ray diffraction, Raman spectroscopy, Mossbauer spectroscopy, X-ray and neutron pair distribution function analysis, and electron microscopy. The results demonstrate that our synthesis technique leads to the formation of chemically uniform single-phase solid solution nanoparticles with cubic spinel structure, confirming intrinsic doping. The local structure of the Fe3O4 NPs is distorted with respect to the cubic inverse-spinel structure, while chemical substitution of Fe by Mn or Ni partially eliminates the local distortions. Magnetic studies showed that, in comparison to nondoped Fe3O4, the saturation magnetization (M-s) of MxFe3-xO4 (M = Mn, Ni) decreases With increasing dopant concentration; while Co-doped samples showed similar M-s. On the other hand, whereas Mn- and Ni-doped nanoparticles exhibit superparamagnetic behavior at room temperature, ferrimagnetism emerges for CoxFe3-xO4 nanoparticles, which can be tuned by the level of Co doping.

• 出版日期2015-5-28