Ac conductivity and relaxation mechanism in Ba0.9Sr0.1TiO3

作者：Singh A K; Barik Subrat K; Choudhary R N P^*; Mahapatra P K

来源：Journal of Alloys and Compounds, 2009, 479(1-2): 39-42.

DOI：10.1016/j.jallcom.2008.12.130

• Solid-state reaction
• XRD
• Ac conductivity
• Electrical relaxation

The ac conductivity and relaxation mechanism in Ba0.9Sr0.1TiO3 ceramics have been investigated systematically. A high-temperature solid-state reaction technique was used to synthesize the compound. The formation of the compound was checked by an X-ray diffraction (XRD) technique. The dielectric permittivity and the loss tangent of the sample were measured in a frequency range from 1 kHz to 1 MHz at different temperatures (30-500 degrees C). A study on dielectric properties reveals the electrical relaxation phenomenon occurs in the material. The activation energy was calculated from the temperature variation of dc conductivity. Studies of frequency and temperature dependence of ac conductivity of the compound suggest that conduction process in the material is thermally activated.

• 出版日期2009-6-24