Abrasive wear comparison of Cr3C2/Ni3Al composite and stellite 12 alloy cladding

作者：Luo He li^*; Karin Gong; Li Shang ping; Cao Xu; Zhang Xi e; Feng Di; Li Chang hai

来源：Journal of Iron and Steel Research International, 2007, 14(5): 15-20.

DOI：10.1016/S1006-706X(08)60044-8

• Ni3Al
• stellite12
• chromium carbide
• composity
• abrasive wear

The room-temperature abrasive wear resistance of Cr3C2/Ni3Al composite and Stellite12 alloy cladding was investigated. Three kinds of tests, designed for different load and abrasive' size, were utilized to understand the wear behaviour of these materials. Under all three wear conditions, the abrasion resistance of Cr3C2/Ni3Al composite cladding is much higher than Stellite 12 alloy. In addition, the wear-resistant advantage of Cr3C2/Ni3Al composite is more obvious when the size of the abrasive is small. The relative wear resistance of Cr3C2/Ni3Al composite increases from 2.44 times to 6 times when the size of the abrasive decreases from 180 mu m to 50 mu m. The good wear resistance of Cr3C2/Ni3Al composite cladding can be mainly attributed to the high hardness, large volume fraction of reinforcement, large reinforcement particles, and size distribution of reinforcement.

• 出版日期2007-9
• 单位钢铁研究总院