Adhesive-Free Transfer of Gold Patterns to PDMS-Based Nanocomposite Dielectric for Printed High-Performance Organic Thin-Film Transistors

作者：Shi Jingsheng; Chan Park Mary B; Li Chang Ming^*

来源：ACS Applied Materials & Interfaces, 2011, 3(6): 1880-1886.

DOI：10.1021/am200058b

• electrode-semiconductor interface
• organic thin-film transistor
• semiconductor-dielectric interface
• transfer printing
• nanocomposite
• PDMS
• titanium oxide nanoparticle

Low-cost, adhesive-free direct transfer of gold patterns onto PDMS-based nanocomposite dielectric layer was investigated to significantly improve contact resistance at electrode-semiconductor interface in organic thin-film transistors (OTFTs). In particular, the nanocomposite film made from PDMS and solution-processable titanium dioxide nanoparticles was applied as dielectric layer in OTFTs, while transfer of gold patterns with a resolution lower than 3 mu m is realized without use of any adhesive but through increased adhesion between gold and nanocomposite film of higher thickness and dielectric constant formed by in situ PDMS cross-linking process. Dielectric constant of the nanocomposite shows a dependence on the ratio of titanium dioxide nanoparticles to PDMS and the dielectric thickness was optimized for the best transfer efficiency. The organic transistors fabricated by this process demonstrate a high mobility of 0.038 cm(2)/(V s) and on/off ratio of 1 x 10(4) to 1 x 10(5). The electrode-semiconductor interface is evaluated by transmission line model to have width-normalized contact resistance of similar to 100 k Omega cm while the inert property of dielectric-semiconductor interface gives low hysteresis (Delta V(th) = 1.2 V) and low threshold voltage (V(th) = -1.3 V) in the devices. This process can be readily adapted into a low-cost mass manufacturing process for printed organic electronics.

• 出版日期2011-6
• 单位南阳理工学院