ANNEALING INFLUENCE ON THE STRUCTURAL AND MAGNETIC PROPERTIES OF Fe73.5Cu1Nb3Si13.5B9 POWDERS

作者：Budeanu L^*; Chiriac H; Lupu N; Neagu M; Borza F

来源：Romanian Reports in Physics, 2016, 68(2): 623-629.

• amorphous magnetic materials
• magnetic powders
• nanocrystalline magnetic materials
• structural properties
• magnetic properties

Results concerning structural and magnetic properties of Fe73.5Cu1Nb3Si13.5B9 powders prepared by mechanical milling of amorphous ribbons are presented. The obtained powder was isothermally annealed in vacuum at temperatures between 400 degrees C and 500 degrees C. The nanocrystalline powder with the lower coercive magnetic field is obtained after annealing 1 hour at 475 degrees C.