(111)-Oriented Co0.8Fe2.2O4+delta thin film grown by pulsed laser deposition: structural and magnetic properties

作者：Khodaei M^*; Ebrahimi S A Seyyed; Park Yong Jun; Choi Sun Hee; Kim CheolGi; Son Junwoo; Baik Sunggi

来源：Journal of Materials Science, 2013, 48(20): 6960-6969.

DOI：10.1007/s10853-013-7504-5

The perfect (111)-oriented Co0.8Fe2.2O4+delta thin films were grown on Pt(111)/Si substrate by pulsed laser deposition technique. Co0.8Fe2.2O4+delta film grown at oxygen pressure of 10 mTorr (optimum condition) has the highest (111)-orientation degree, the lowest surface roughness, uniformly compacted nanosize grain-feature structure (50-80 nm), and the highest magnetization. The Fe K-edge X-ray absorption near edge structure analyses revealed that, in Fe-doped CoFe2O4 film, the Fe also exists as Fe3+ (Co0.8Fe2.2O4+delta ), which affects the lattice parameter as well as magnetic properties. The magnetic properties (saturation magnetization, coercivity, and squareness) of Co0.8Fe2.2O4+delta thin film are significantly higher than those of CoFe2O4 film. Moreover, the (111)-oriented Co0.8Fe2.2O4+delta thin film demonstrates strong in-plane magnetic anisotropy, which results from orientation, as well as the stress-induced magnetic anisotropy.

• 出版日期2013-10