摘要
SrRuO3 films were prepared using pulsed laser deposition on different substrates (z-cut Quartz, (001) SrTiO3 and (001) LaAlO3) in this work. We have observed greatly enhanced perpendicular coercivity over 2 T in nanocrystalline Si Ru03 thin films with a thickness of 60 rim deposited at 600 degrees C on quartz substrates compared to epitaxial thin films (60 nm) on (001) SrTiO3 and (001) LaAlO3 substrates. Our experiments have also shown that a lattice strain may result in reduced Curie temperature and enhanced saturation magnetization. The spin glass like behavior is observed in the nanocrystalline thin films. The augmentation of the coercivity is possibly associated with nanocrystalline nature and the spin glass like phenomena in the films.
- 出版日期2015-1-15