The effect of polyethylene glycols on zinc dissolution at 50 degrees C in 0.5 M H2SO4 containing Co, Sb and Ge

作者：Karavasteva M S^*

来源：Hydrometallurgy, 2011, 106(1-2): 1-4.

DOI：10.1016/j.hydromet.2010.10.010

• Polyethylene glycols
• Zinc dissolution
• Impurities Co
• Sb and Ge

The effect of the structure of polyethylene glycols [i.e. the presence of alkylphenyl group (APG) and the variation in the number of ethylene oxide groups (EOG) in the molecule] on the kinetics of zinc dissolution at 50 degrees C in 0.5 M H2SO4 containing impurities more positive than zinc (Co, Sb and Ge) was studied. It was found that nonylphenyl-polyethylene glycol with 15 EOG and APG in the molecule (S1), polyethylene glycols with 9 EOG (S2) and 45 EOG (S3) decrease zinc dissolution rate. The effect of surfactants decreases in order S1 > S3 > S2. The effect caused by the presence of nonylphenyl group in Si surpasses that caused by the three times higher number of EOG in S3. The addition of S1 and S3 substantially inhibit the deposition (cementation) of impurities on zinc surface thus decreasing their effect on zinc dissolution. Zinc surface morphology was examined after dissolution using scanning electron microscopy (SEM). Due to Si and S3 adsorption, zinc surface remains compact (without holes and cracks) which strikingly reduces the quantity of dissolved metal.
The influence of S1 and S3 on zinc dissolution in the presence of Co, Sb and Ge confirms their inhibition effect on the negative action of above mentioned impurities during electrowinning stage in zinc hydrometallurgy.

• 出版日期2011-2