摘要
A red La(OH)(3)/TiO2:B,N composite photocatalyst with broad-band visible-light-response was successfully synthesized through a three-step synthetic route. Structural, morphologic, optical and surface characteristics of the as-prepared photocatalysts were characterized by XRD, SEM, TEM, UV-vis, BET and XPS measurements. The 1.5% La added sample exhibited a high photocatalytic performance (48 mu mol h(-1)) in the presence of K2CO3 as the sacrificial agent under visible-light irradiation (lambda > 400 nm), which is almost a 24-fold increase compared with the sample without La added.