Nanocrystalline Si/SiO2 core-shell network with intense white light emission fabricated by hot-wire chemical vapor deposition

作者：Matsumoto Y^*; Dutt A; Santana Rodriguez G; Santoyo Salazar J; Aceves Mijares M

来源：Applied Physics Letters, 2015, 106(17): 171912.

DOI：10.1063/1.4919527

We report the fabrication of a stable Si/SiO2 core-shell network using hot-wire chemical vapor deposition on a silicon substrate at a relatively low substrate temperature of 200 degrees C. Structural investigations using transmission electron microscopy and X-ray diffraction confirm the presence of nanocrystalline silicon and silicon dioxide quantum dots in the form of a core-shell network embedded in the amorphous SiOx matrix, while selected area electron diffraction confirms the formation of a core-shell structure. The core-shell structure exhibits a bright white emission that can be seen with the unaided eye at room temperature without any post-annealing treatments, and the observed photoemission does not alter in color or intensity after prolonged laser exposure. Additional measurements are performed while varying the laser power and optical gain is found in the as-deposited material. Intense stable white luminescence is observed and shows the prospective for various optical and biological applications in the future.

• 出版日期2015-4-27