Morphology and properties of poly(lactic acid-co-glycolic acid) film improved by blending with poly(gamma-benzyl L-glutamate)

作者：Zhu Guoquan; Wang Fagang^*; Xu Kejing; Gao Qiaochun; Liu Yuying

来源：Research on Chemical Intermediates, 2015, 41(3): 1647-1655.

DOI：10.1007/s11164-013-1300-3

• Morphology
• Properties
• Poly(lactic acid-co-glycolic acid)
• Polypeptide
• Blend
• Film

A series of poly(lactic acid-co-glycolic acid) (PLGA)/poly(gamma-benzyl l-glutamate) (PBLG) blend films were prepared by casting the polymer blend solution in chloroform. Surface morphologies of the PLGA/PBLG blend films were investigated by scanning electron microscopy. Thermal, mechanical, and chemical properties of PLGA/PBLG blend films were studied by differential scanning calorimetry, thermogravimetric analysis, tensile tests, and surface contact angle tests. The results displayed that when PBLG mole content is 4 %, the tensile strength and the maximum decomposition temperature of the polymer blend film are 20.2 MPa and 359 A degrees C, respectively, suggesting that the polymer blend film holds both a better mechanical property and a better thermal property.

• 出版日期2015-3
• 单位山东理工大学