Determination of magnetic domain state of carbon coated iron nanoparticles via Fe-57 zero-external-field NMR

作者：Manjunatha M; Kumar Rajeev; Sahoo Balaram^*; Damle Ramakrishna; Ramesh K P^*

来源：Journal of Magnetism and Magnetic Materials, 2018, 453: 125-131.

DOI：10.1016/j.jmmm.2018.01.017

• Magnetic domain state
• Critical single-domain size
• Carbon-coated iron
• Fe-57-IFNMR
• Magnetic domain dynamics

The magnetic domain state of carbon coated iron nanopowder (Fe@C) was studied by the internal field nuclear magnetic resonance (IFNMR) at 77 K using the spin echo technique. The structure and magnetic properties of the sample were further characterized by scanning electron microscopy (SEM), X-ray diffraction (XRD), Mossbauer spectroscopy, vibrating sample magnetometry (VSM), thermogravimetric analysis (TGA) and Raman Spectroscopy. The obtained IFNMR results of Fe@C powder were compared with that of micron sized carbonyl iron (CI) and electrolytic iron (EI) powders. The calculated critical size of the single domain iron particles in Fe@C is similar to 16 nm. A higher enhancement in echo amplitude was observed due to better response of the domain walls of multidomain particles in comparison to the single domain particles. The echo signal of CI and EI particles exhibit a single narrow intense peak corresponding to the domain walls, whereas Fe@C exhibits two low amplitude peaks at two different frequencies: a low frequency (46.6 MHz) peak corresponds to the response of the domain walls of the multidomain particles and the other high frequency (47.2 MHz) signal (a shoulder) corresponding to the response of the magnetic nuclei inside the domain. Our results help in determining the domain state of iron-based magnetic particles using Fe-57-IFNMR.

• 出版日期2018-5-1